AUSTENITIC STAINLESS STEELS - BS3100:1991
| Compositional
Analysis % |
Mechanical Properties minimum |
| Grade |
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
Nb |
|
Lower Yield (N/mm2) |
Tensile Strength (N/mm2) |
Elongation A% |
| 302C25 |
0.12 |
1.5 |
2.0 |
0.04 |
0.04 |
17-21 |
- |
8
min |
- |
240 |
480 |
26 |
| 304C12 |
0.03 |
1.5 |
2.0 |
0.04 |
0.04 |
17-21 |
- |
8-12 |
|
215 |
430 |
26 |
| 304C15 |
0.08 |
1.5 |
2.0 |
0.04 |
0.04 |
17-21 |
- |
8-12 |
|
215 |
480 |
26 |
| 347C17 |
0.08 |
1.5 |
2.0 |
0.04 |
0.04 |
18-21 |
- |
9-12 |
8
x C |
215 |
480 |
22 |
| 316C12 |
0.03 |
1.5 |
2.0 |
0.04 |
0.04 |
17-21 |
2-3 |
9
min |
|
215 |
430 |
26 |
| 316C16 |
0.08 |
1.5 |
2.0 |
0.04 |
0.04 |
17-21 |
2-3 |
9
min |
|
240 |
480 |
26 |
| 318C17 |
0.08 |
1.5 |
2.0 |
0.04 |
0.04 |
17-21 |
2-3 |
|
8
x C |
240 |
480 |
18 |
Composition % is maximum unless shown otherwise